Polyurethane Pu Top Coat Set VP510

Discover the excellence of our VP510.XX.0000 PU coating for wood, coded as VP510, a two-component PU set designed to meet increasing customer demands for high scratch resistance and a homogeneous matt appearance while maintaining an optimal price/performance balance.

This topcoat product sets itself apart with transparent film, exceptional scratch resistance, a soft touch, and a high body, ensuring a protective and decorative finish on all indoor wooden surfaces. Elevate your woodworking projects with Woodemotions, where quality and aesthetics converge seamlessly.

Product Properties

Transparent Film

The varnish skillfully forms a crystal-clear film, allowing the innate beauty of the wood to shine through. This transparency adds a touch of elegance to your wood surfaces, enhancing their natural allure.

High Scratch Resistance

Meticulously engineered for outstanding scratch resistance, this varnish ensures the longevity and durability of your wood finish. Enjoy peace of mind knowing your surfaces are protected against everyday wear and tear.

Homogeneous Matt Appearance

Immerse your wood projects in a consistently matte finish that not only meets but exceeds aesthetic expectations. The homogeneous appearance creates a seamless look, contributing to the overall sophistication of your wooden surfaces.

Soft Touch

Experience a luxurious and inviting tactile sensation as the varnish imparts a soft touch to your coated wood. This feature elevates the sensory experience, making your wood surfaces not just visually appealing but also delightful to the touch.

High Body

Elevate the quality of your wood surfaces with the varnish's high body, adding substantial depth and character. This unique property enhances the overall feel and appearance, ensuring a distinctive and premium finish for your woodworking projects.

Application and Usage Guide for VP510.XX.0000 PU Top Coat

VP510.XX.0000 Polyurethane Top Coat effortlessly integrates into our PU wood coating collection, enhancing the range with its exceptional features. Elevate your woodworking projects with this topcoat, adding a protective and decorative layer to indoor wooden surfaces.

Surface Preparation

Begin by ensuring the wooden surface is clean, dry, and free from dust and contaminants. Sand the surface using fine-grit sandpaper (e.g., 220 grit) for a smooth foundation.

Mixing the Varnish

Before application, thoroughly mix the VP510.XX.0000 PU varnish , following the recommended ratio with the Polyurethane Hardener (HP600.00). The standard mixing ratio is 100 parts varnish to 50 parts hardener.

Choosing the Application Method

Select your preferred application method based on the project requirements. The Polyurethane Varnish Matt Series offers versatility, allowing for application with airmix or conventional spray guns.

Application Process

● For Airmix Spray Gun

Adjust the gun settings for an even and controlled spray. Maintain a consistent distance of approximately 6-8 inches from the surface. Apply thin, overlapping coats to achieve the desired coverage.

● For Conventional Spray Gun

Adjust the gun settings according to the manufacturer's recommendations. Apply the varnish evenly in smooth, sweeping motions.

Drying Process

Drying Stage	Time Range
Dust-Free	10 - 12 minutes
Touch Dry	25 - 30 minutes
Stackable	3 - 4 hours

Drying Time

Allow the applied coats to dry according to the specified drying times:

Dust-Free in 10-12 minutes
Touch Dry in 25-30 minutes. Ensure proper ventilation during the drying process.

Stacking (500 kg/m²)

Once the varnish is completely dry, typically after 3-4 hours, surfaces become stackable with a load-bearing capacity of 500 kg/m². Exercise caution to prevent any damage during this period.

Additional Coats (Optional)

If a higher level of protection or a different finish is desired, consider applying additional coats after the initial ones have dried completely.

Curing and Full Protection

Allow the coated wooden surfaces to cure fully, providing maximum protection. The exceptional scratch resistance and longevity of the wood finish will become evident over time.

Technical Specifications Of Genc Polyurethane Varnish Matt Series

Product	Polyurethane Hardener	Mixing Ratio	Non-Volatile Matter I.Comp (%)	Non-Volatile Matter I + 2 Comp (%)	Viscosity (KU, 25°C)	Density (g/cm³)	Pot Life (20°C, h)
VP510.XX.0000	HP600.00	100/50	46 ± 2	39 ± 2	50 - 60	1.02 ± 0.03	5
VP509.XX.0000	HP600.00	100/50	43 ± 2	37 ± 2	60 - 70	0.995 ± 0.03	4
Tp100 Thinner		40% to 50%

VP510.XX.0000

A well-balanced mixing ratio of 100 parts varnish to 50 parts hardener ensures optimal performance.
The non-volatile matter in the initial component is 46 ± 2%, and the combination of both components results in 39 ± 2%, contributing to a durable and resilient finish.
The viscosity at 25°C ranges from 50 to 60 KU, providing ease of application.
With a density of 02 ± 0.03 g/cm³, the varnish offers substance without compromising on quality. The pot life at 20°C is approximately 5 hours, allowing sufficient time for precise application.

VP509.XX.0000

This variant maintains the 100/50 mixing ratio for consistent results.
The non-volatile matter in the initial component is 43 ± 2%, while the total in both components is 37 ± 2%, ensuring a resilient finish.
The viscosity at 25°C ranges from 60 to 70 KU, providing versatility in application.
With a density of 995 ± 0.03 g/cm³, it balances substance and quality.
The pot life at 20°C is approximately 4 hours, allowing efficient application and ensuring quality results.

Explore the premium VP510.XX.0000 Polyurethane Varnish Matt Series for your wood projects, ensuring exceptional quality and a matte finish. Check out Woodemotions for competitive PU paint prices in Pakistan, delivering top-notch solutions for your woodworking needs.